Araldite® Epoxy,
Urethane
& Methacrylate Adhesives Specifications
View
the print-friendly version of this spec table (pdf)
View
the Araldite Applications & Resistance Properties
(pdf)
Note: All
product titles link to the respective product pages
|
Product
Number |
Mix
Ratio
Resin to
Hrd'nr
by wt. |
Mix
Ratio
Resin to
Hrd'nr
by vol. |
Gel
Time
(min) |
Light
Handling
Time
|
Cure
Time
at 73ºF
(hr) |
Cure
Time
at 140ºF
(min) |
Mixed
Viscosity
(cps.) |
Hardness
(Shore D) |
Lap
Shear
Strength
(psi) |
Peel
Strength
(pli)
|
Tensile
Strength
(psi) |
Servicable
Temperature
Typical/Max
(ºF) |
Epoxy
Adhesives |
2010 |
100:100 |
100:100 |
10 |
30
min |
3 |
25 |
80,000 |
- |
3,300 |
46 |
- |
105/175 |
2011 |
100:80 |
100:100 |
105 |
7
hours |
10 |
45 |
45,000 |
80 |
2,700 |
29 |
4,800 |
110/175 |
2012 |
100:100 |
100:100 |
4 |
20
min |
1.75 |
25 |
30,000 |
82 |
2,700 |
31 |
- |
105/175 |
2013 |
100:60 |
100:100 |
75 |
4
hours |
10 |
40 |
Paste |
80 |
2,600 |
23 |
5,000 |
110/160 |
2014 |
100:50 |
100:50 |
40 |
4
hours |
5 |
25 |
90,000 |
84 |
2,600 |
17 |
5,500 |
185/285 |
2015 |
100:100 |
100:100 |
40 |
4
hours |
10 |
40 |
Paste |
75 |
2,400 |
29 |
3,400 |
150/212 |
2043 |
100:100 |
100:100 |
1 |
5
min |
1 |
- |
20,000 |
83 |
3,100 |
- |
- |
flexible |
Fastweld
10 |
100:100 |
100:100 |
4 |
10
min |
4 |
- |
250,000 |
85 |
2,840 |
- |
3,850 |
- |
AW1258/HV1258 |
100:100 |
100:100 |
23 |
4
hours |
6 |
- |
Paste |
89 |
2,840 |
- |
5,600 |
- |
AW1253/HV1253 |
100:82 |
100:100 |
20 |
4
hours |
6 |
- |
Paste |
73 |
1,990 |
- |
2,130 |
- |
AY557/HY557 |
100:100 |
100:100 |
4 |
10
min |
4 |
- |
14,000 |
83 |
2,560 |
- |
4,630 |
- |
|
|
100:100 |
60 |
5.5 hour |
16 |
60 |
Paste |
75 |
2,500 |
- |
2,290 |
176 |
8579 |
100:40 |
100:40 |
60 |
8 hour |
8 |
- |
125,000 |
- |
2,500 |
- |
- |
248 |
Methacrylate
Adhesives |
2021 |
100:90 |
100:100 |
3 |
8
min |
20
min |
- |
45,000 |
78 |
3,200 |
63 |
- |
150/230 |
2022 |
100:94 |
100:100 |
10 |
18
min |
30
min |
- |
60,000 |
75 |
3,600 |
23 |
- |
110/212 |
2024 |
100:11 |
100:10 |
3 |
10
min |
15
min |
- |
180,000 |
- |
2,300 |
29 |
2900 |
105/212 |
Polyurethane
Adhesives |
2026 |
100:100 |
100:100 |
5 |
1
hour |
4 |
30 |
10,000 |
- |
3,000 |
29 |
2600 |
flexible |
2027 |
100:97 |
100:100 |
8 |
1.5
hours |
10 |
40 |
Paste |
- |
2,000 |
46 |
2050 |
77/140 |
2040 |
93:100 |
100:100 |
15 |
10
hours |
24 |
120 |
50,000 |
30 |
1,700 |
- |
1,100 |
flexible |
2041 |
80:100 |
100:100 |
12 |
4
hours |
16 |
120 |
50,000 |
85A |
2,800 |
- |
2,100 |
flexible |
2042 |
80:100 |
100:100 |
2.5 |
1
hour |
6 |
60 |
50,000 |
85A |
2,800 |
- |
2,100 |
flexible |
2042-1 |
80:100 |
100:100 |
3 |
1 hour |
6 |
- |
- |
- |
- |
- |
- |
flexible |
AW8680/HV8685 |
80:100 |
100:100 |
8-10 |
2
hours |
12 |
- |
34,000 |
40 |
2,900 |
- |
2,100 |
- |
Cure Times
= Time required for bond to reach 50% of final shear strength
of 150 psi or greater
Lap Shear Strength = After 7-day cure @ 73ºF on aluminum
Peel Strength = After 7-day cure @ 73ºF on aluminum
Serviceable Temperature = Typical Tg Value/Max Temperature giving
LSS of 750 psi
|
|