Epoxy Laminating Resin
Specifications
View
the Freeman Epoxy Tooling Resins Brochure (pdf)
View
the RenLam Epoxy Laminating Resin Specifications
(pdf)
Room
Temperature Laminating Resins |
Product
Number
|
Mix
Ratio
(by wt.)
Resin:
Hardener
|
Mix
Ratio
(by vol.)
Resin:
Hardener
|
Gel
Time
(min.)
@ 72°F
|
Demold
Time
(hours)
@ 72°F
|
Hardness
(Shore D)
|
Mixed
Viscosity
(cps)
|
Specific
Gravity
(mixed)
|
Density
(g/cc)
|
Volumetric
Yield
(cu. in. / lb.)
|
Shrink
(in / in)
|
Compressive
Strength
(psi)
|
Flexural
Strength
(psi)
|
Flexural
Modulus
(psi)
|
Tensile
Strength
(psi)
|
C.T.E.
(in / in / °F) *
|
Deflection
Temp. (°F)
|
Tg
(°F)
|
Freeman
601
|
100:10
|
100:14
|
28
|
24
|
88
|
3,000
|
1.39
|
|
19.9
|
-
|
39,900
|
34,600
|
-
|
25,000
|
-
|
128°
|
|
Freeman
605 - 15
|
100:16
|
4.99:1
|
20
|
24
|
82
|
2,850
|
1.3
|
|
21.28
|
-
|
40,000
|
33,500
|
1.8
x 106
|
25,300
|
-
|
188°
|
|
Freeman
605 - 45
|
100:20
|
3.8:1
|
37
|
24
|
86
|
2,800
|
1.284
|
|
21.56
|
-
|
40,000
|
33,500
|
1.8
x 106
|
25,300
|
-
|
188°
|
|
Freeman
690
|
100:33
|
100:37
|
90
|
24
|
85
|
1,445
|
1.1
|
|
25
|
-
|
26,500
|
39,900
|
1.3
x 106
|
35,500
|
-
|
180°
|
|
| RenLam
286 |
100:18 |
100:26 |
20-30 |
24
|
90
|
2,400 |
|
1.42 |
19.6 |
|
40,400 |
35,300 |
|
26,500 |
- |
|
- |
RenLam
1135 /
Ren 1135 |
100:33 |
100:40 |
7 |
24
|
90
|
3,250 |
|
1.23 |
22.5 |
|
- |
- |
|
- |
- |
|
- |
RenLam
1700-1 /
Ren 1700-1 |
100:26 |
100:28 |
20 |
24
|
90
|
2,000 |
|
1.13 |
24.5 |
|
28,100 |
37,000 |
|
26,000 |
1.00
x 10-5 |
|
128 |
RenLam
1700-1 /
Ren 956 |
100:23 |
100:25 |
36 |
24
|
89
|
2,000 |
|
1.13 |
24.5 |
|
24,700 |
40,700 |
|
34,900 |
0.97
x 10-5 |
|
129 |
RenLam
1710 /
Ren 1710 |
100:16 |
100:23 |
22 |
24
|
90
|
3,500 |
|
1.35 |
20.5 |
|
23,000 |
30,000 |
|
25,000 |
1.20
x 10-5 |
|
129 |
RenLam
1710 /
Ren 956 |
100:16 |
100:23 |
35 |
24
|
-
|
2,000 |
|
- |
- |
|
26,900 |
32,900 |
|
25,000 |
0.81
x 10-5 |
|
- |
RenLam
1720 /
Ren 956 |
100:15 |
- |
40 |
24
|
90
|
3,200 |
|
1.34 |
20.5 |
|
- |
36,000 |
|
- |
1.02
x 10-5 |
|
- |
| RenLam
3270 |
100:14 |
100:20 |
28 |
24
|
84
|
3,600 |
|
1.70 |
16.3 |
|
23,000 |
30,000 |
|
28,000 |
1.10
x 10-5 |
|
140 |
RenLam
177-114 /
Ren 956 |
100:24 |
- |
38 |
24
|
90
|
800 |
|
1.15 |
24.1 |
|
26,000 |
39,000 |
|
36,000 |
0.93
x 10-5 |
|
- |
High
Temperature Laminating Resins |
Product
Number
|
Mix
Ratio
(by wt.)
Resin:
Hardener
|
Mix
Ratio
(by vol.)
Resin:
Hardener
|
Gel
Time
(min.)
@ 72°F
|
Demold
Time
(hours)
@ 72°F
|
Hardness
(Shore D)
|
Mixed
Viscosity
(cps)
|
Specific
Gravity
(mixed)
|
Density
(g/cc)
|
Volumetric
Yield
(cu. in. / lb.)
|
Shrink
(in / in)
|
Compressive
Strength
(psi)
|
Flexural
Strength
(psi)
|
Flexural
Modulus
(psi)
|
Tensile
Strength
(psi)
|
C.T.E.
(in / in / °F) *
|
Deflection
Temp. (°F)
|
Tg
(°F)
|
Freeman
917
|
100:10
|
100:13
|
52
|
24
|
92
|
4,000
|
1.46
|
|
19
|
-
|
24,500
|
30,574
|
1.6
x 106
|
23,000
|
2.56
x 10-5
|
301°
|
|
RenLam
4005 /
Ren 1500 |
100:14 |
100:15 |
50 |
24
|
90
|
1,900 |
|
1.19 |
23.3 |
|
28,000 |
35,000 |
|
26,000 |
0.85
x 10-5 |
|
289 |
RenLam
4014 /
Ren 1500 |
100:11 |
100:14 |
55 |
24
|
90
|
4,000 |
|
1.34 |
20.8 |
|
28,000 |
34,000 |
|
24,000 |
1.41
x 10-5 |
|
333** |
RenLam
4017 /
Ren 1510 |
100:15 |
- |
90 |
24
|
93
|
8,000 |
|
1.42 |
19.6 |
|
44,000 |
77,000 |
|
80,000 |
3.4
x 10-6 |
|
350** |
RenLam
8105 /
Medium Hardener |
100:28 |
100:32 |
120 |
24
|
91
|
3,400 |
|
- |
- |
|
29,500 |
37,400 |
|
23,100 |
2.5
x 10-5 |
|
294** |
RenLam
8105 /
Slow Hardener |
100:29 |
100:32 |
180 |
24
|
90
|
5,500 |
|
- |
- |
|
30,900 |
40,200 |
|
22,200 |
3.4
x 10-5 |
|
295** |
RenLam
1310 /
Ren 1520 |
100:32 |
- |
960 |
24
|
91
|
7,700 |
|
1.25 |
22.3 |
|
45,000 |
78,000 |
|
100,000 |
3.4
x 10-6 |
|
446** |
RenLam
188-10 /
Ren 188-10 |
100:11 |
100:14 |
55 |
24
|
90
|
4,000 |
|
1.33 |
20.8 |
|
25,000 |
30,000 |
|
22,200 |
1.1
x 10-5 |
|
290 |
ASTM
|
-
|
-
|
D-2471
|
-
|
D-2240
|
D-2393
|
D-792
|
D-792
|
D-792
|
D-2566
|
D-695
|
D-790
|
D-790
|
D-638
|
D-696
|
D-648
|
D-648
|
|